Notice: Function _load_textdomain_just_in_time was called incorrectly. Translation loading for the updraftplus domain was triggered too early. This is usually an indicator for some code in the plugin or theme running too early. Translations should be loaded at the init action or later. Please see Debugging in WordPress for more information. (This message was added in version 6.7.0.) in /home/hg48noczj0hc/public_html/wp-includes/functions.php on line 6114

Notice: Function _load_textdomain_just_in_time was called incorrectly. Translation loading for the wordpress-seo domain was triggered too early. This is usually an indicator for some code in the plugin or theme running too early. Translations should be loaded at the init action or later. Please see Debugging in WordPress for more information. (This message was added in version 6.7.0.) in /home/hg48noczj0hc/public_html/wp-includes/functions.php on line 6114
Levels of nickel phosphorous plating - High to Low-Phos Electroless

These are terms used in the electroless nickel plating process.  Due to its exceptional corrosion resistance and high hardness, this process is ideal for items such as valves and pump parts extending the life of components exposed to severe conditions of service.

There are different levels of nickel phosphorous plating:

  • Low-Phosphorus content between 3 and 7%. These coatings have excellent high wear resistance and corrosion resistance.

 

  • Mid-Phosphorus content between 9 and 12%. Corrosion protection and abrasion resistance are good enough for most applications. The plating bath works particularly economically.

 

  • High-Phosphorus content between 10 and 13%. The coatings are very ductile and corrosion resistant. They fulfill the highest demands for corrosion resistance against chlorides and simultaneous mechanical stress. High Phosphorous electroless nickel is standard in industries that require resistance to strongly acidic corrosive environments

Begin investing from just $250 and explore global markets Skyline Nexus Pro Platform

At Stat Processing we specialize in high-phosphorous content.  By specializing in this process our products have a harder and better wearing surface. The high-phos process is more resistant to corrosion and will have a higher salt spray testing number (1000 hours).

Contact the professionals at Stat Processing today to determine the best solution for your plating needs.